太古水泥耐磨防裂填料白色氧化鋁砂220#

電熔氧化鋁又稱白剛玉,用于涂料行業，因其耐磨性好，吸油率低，硬度高等優點，廣泛用于涂料填料。電熔氧化鋁是將純度99%含量的工業氧化鋁在電弧爐里經2050度高溫熔融冶煉結晶而來，因此電熔氧化鋁又被稱為電熔剛玉。電熔氧化鋁純度高、自銳性好、耐酸堿腐蝕、耐高溫、熱態 性能穩定它硬度略高于棕剛玉，韌性稍低，切削力強。

White electro corundum F180, F220, and F240 are suitable for two-component microcement group A filler. It has better wear resistance, corrosion resistance, and high-temperature resistance than quartz sand. Microcement, also known as Taikoo cement, is a new type of building material that has emerged in recent years. It can achieve seamless integration of the ground, wall, and roof. It is similar to polyurethane water-based flooring. Microcement is a decoration material made by fusing micro cement with resin and adding wear-resistant materials. It has advantages such as good wear resistance, waterproofing, corrosion resistance, and antibacterial properties.

電熔氧化鋁的主要性能特點：

在涂料產品中的配方中，除了樹脂基料以外，往往會添加一些填料起到填充、調節涂料相關性能等作用。作為涂料的填充材料，需要符合以下幾個基本要求：

1. 白度要高。不能影響涂料基料和顏料的顏色調配。

2. 分散性好。易分散的填料不僅可以降低涂料生產時分散填料的時間和成本，而且有利于涂料性能的發揮。

3. 化學穩定性和惰性。填料不會與涂料中的基料、顏料和其他填料發生反應。

4. 吸油率要低。低吸油率有利于提高涂料的臨界顏料體積濃度，節約樹脂基料。同時，與市場上主流的其他低吸油的顏料相匹配。

5. 填料的粒度要準確，粒度范圍要盡量窄、盡量的集中。粒度窄的填料粉末能在涂料中起到空間位隔作用，使涂料中的各種材料顆粒更加均勻地分布。有助于保持涂料的性能一直性。

6. 流動性。良好的流動性（流平性），可以防止涂料在放置和存貯時不產生沉淀，有利于涂料的施工。

7. 比表面積適當，比表面積影響涂料的黏度、流動性、分散穩定性、沉降度和吸油量等性能指標。

電熔氧化鋁是經過高溫電熔結晶形成的氧化鋁材料，也被稱為電熔白剛玉微粉，化學性能符合作為填料的穩定性特點。它作為水性涂料、環氧涂料、聚氨酯涂料、氟碳涂料、氟碳粉末涂料的填料，具有以下優點：

1. 顏色白度高

2. 電熔氧化鋁微粉進過水力溢流分級，產品流動性和分散性好。

3. 化學穩定性強，不與酸堿等物質產生化學反應。

4. 吸油率低，經我公司客戶檢測，吸油率10%以內。

5. 水分工藝生產的電熔氧化鋁，粒度范圍集中，對大顆粒進行有效控制，保證顆粒的均勻一致。

6. 電熔氧化鋁的耐火溫度高，熱穩定性強。

7. PH值為中性。

8. 電熔氧化鋁微粉的硬度高，耐磨性強，可以增強涂料的耐磨性能。

9. 我廠生產的電熔氧化鋁微粉粒度齊全，水分微粉從63微米到0.5微米均可以提供。

電熔氧化鋁的化學成分（典型指標）：

電熔氧化鋁的物理性能：

涂料用電熔氧化鋁的常用型號：

180目，220目，240目，280目，1200目，1500目，2000目，2500目。

涂料用電熔氧化鋁應用范圍：

1. 水性環氧地坪漆

2. 停車場聚氨酯涂料（PU涂料）

3. 粉末涂料

4. 環氧地坪砂漿涂料。

5. 其他耐磨涂料等。